[口頭報告]Study on the oxidation film formation mechanism and performance of MoSi2-ZrB2-SiC coating on Nb alloy surface under high temperature environment
Study on the oxidation film formation mechanism and performance of MoSi2-ZrB2-SiC coating on Nb alloy surface under high temperature environment
編號：253
稿件編號：305 訪問權限：僅限參會人
更新：2024-05-21 11:54:35
瀏覽：172次
口頭報告
報告開始：2024年05月30日 17:50 （Asia/Shanghai）
報告時間：10min
所在會議：[S7] Minerals and Advanced Energy Materials ? [S7-1] Afternoon of May 30th
暫無文件
摘要
MoSi2-ZrB2-SiC antioxidant coatings were prepared on niobium surfaces using industrial waste molybdenum silicide rods, ZrB2 and SiC as raw materials by SPS. To study the microstructure, phase composition and high temperature oxidation behavior of the coatings at 1000℃, 1200℃, 1400℃ and 1600℃.The results show that an obvious connecting layer is formed between the coating and the substrate prepared from waste molybdenum silicide rods, ZrB2 and SiC powder. With the increase of oxidation time, the coating gradually thickened with the increase of oxidation temperature, the oxide film gradually increased, the ZrO2 particles gradually increased, and the transition layer formed between the Nb substrate and the coating gradually thickened. The waste MoSi2 contains Al2O3 and SiO2, Al2O3 has a good modifying effect, while SiO2 glass promotes liquid-phase sintering and seals defects in the coating. The MoSi2-ZrB2-SiC composite coatings have good high-temperature oxidation resistance.
關鍵字
reuse; waste molybdenum silicide rods; discharge plasma sintering; oxidation resistance; niobium matrix